SPECIAL POLYETHER POLYOL
| Trademark | ZR-001 | 10LD28Z | 10LD36M | 10LD28X (10LD28XM) | ||
| Hydroxyl value mgKOH/g | 24-28 | 22.0-26.0 | 34.0-38.0 | 26.0-30.0 | ||
| Acid value mgKOH/g | – | – | W 0.10 | W 0.05 | ||
| Water content
% |
W 0.10 | W 0.10 | W 0.05 | W 0.05 | ||
| PH | 6.5-10 | 6.5-10 | 5-7 | 5-7 | ||
| Viscosity
mPa • s/25eC |
2000-3000 | 1800-2500 | 900-1400 | 700-1000 | ||
| K+
mg/kg |
Solid content | 25-29% | Solid content | 29-33% | W 5 | W 5 |
| Colourity
APHA |
W 50 | W 50 | ||||
| Functionality | 3 | 3 | 3 | 2 | ||
| Molecular weight | – | – | 5000 | 4000 | ||
| Application | Used in flame-retardant high resilience form, cold molded flexible foam, semi-rigid foam, self-skinning foam, reacting injection molded products, etc. | Used in flame-retardant high resilience form, cold molded flexible foam, semi-rigid foam, self-skinning foam, reacting injection molded products, etc. | Sponge feeling agent. | Sponge next to skin.e.g. sponge of bra. underwear lining. | ||
| Feature | Structural flame-retardant POP that can effectively improve the flame retardancy and supporting capacity of high resilience foam when mixes with high activity PPG. Comparing with common POP. these two product have extremely higher opening ability. Please mind to avoid the collapse of foam caused by its excessive opening capacity when produce high resilience foam. | Structural flame-retardant POP with better retardancy and reaction liquidity compared with ZR001, this product has more adaptive under the Low mold temperature. | This product has a good sense of hand and hydrophilicity. It is suitable for the preparation of various types of flat gas and non thermal slow rebound foam. | Enhancing tensile strength and personal comfort of the sponge. | ||
| Note: please read the above information carefully and once you use the polyol in area that doesn’t involve in the mentioned scope,please consuit us first | ||||||